Dilition as funcion of welding corrent in deposits of tubular coated electrodes for hardfacing of sugar industry component´s
Keywords:
Coated tubular electrode, Hardfacing, WeldingAbstract
It is carried out the determination of geometry of deposits of coated tubular electrodes for hardfacing of pieces in sugar industry. Two versions of coated tubular electrodes (ferroalloy particle size in the soul d”0,1 mm and
in the range of 0,1- 0,25 mm) are evaluated. This study is made in comparative way, using the DIN E60-10 Z commercial coated electrode, which has same diameter (4mm) and same application (hardfacing, widely applied in sugar industry) as this studied. The Coefficient of Dilution is obtained as the ratio of penetration area and total fused area. Starting of the dilution is obtained the composition of de alloying elements in the deposits.
Downloads
Download data is not yet available.
Downloads
Published
2009-04-01
How to Cite
Cruz-Crespo, A., Scotti, A., Rodríguez-Pérez, M., & Ortiz-Méndez, T. (2009). Dilition as funcion of welding corrent in deposits of tubular coated electrodes for hardfacing of sugar industry component´s. Centro Azúcar Journal, 36(3). Retrieved from http://centroazucar.uclv.edu.cu/index.php/centro_azucar/article/view/479
Issue
Section
Original Articles